Evaluating the in vitro wettability and coefficient of friction of a novel and contemporary reusable silicone hydrogel contact lens materials using an in vitro blink model.

PURPOSE: To evaluate the in vitro wettability and coefficient of friction of a novel amphiphilic polymeric surfactant (APS), poly(oxyethylene)-co-poly(oxybutylene) (PEO-PBO) releasing silicone hydrogel (SiHy) contact lens material (serafilcon A), compared to other reusable SiHy lens materials. METHODS: The release of fluorescently-labelled nitrobenzoxadiazole (NBD)-PEO-PBO was evaluated from serafilcon A over 7 days in a vial. The wettability and coefficient of friction of serafilcon A and three contemporary SiHy contact lens materials (senofilcon A; samfilcon A; comfilcon A) were evaluated using an in vitro blink model over their recommended wearing period; t = 0, 1, 7, 14 days for all lens types and t = 30 days for samfilcon A and comfilcon A (n = 4). Sessile drop contact angles were determined and in vitro non-invasive keratographic break-up time (NIKBUT) measurements were assessed on a blink model via the OCULUS Keratograph 5 M. The coefficient of friction was measured using a nano tribometer. RESULTS: The relative fluorescence of NBD-PEO-PBO decreased in serafilcon A by approximately 18 % after 7 days. The amount of NBD-PEO-PBO released on day 7 was 50 % less than the amount released on day 1 (6.5±1.0 vs 3.4±0.5 µg/lens). The reduction in PEO-PBO in the lens also coincided with an increase in contact angles for serafilcon A after 7 days (p < 0.05), although there were no changes in NIKBUT or coefficient of friction (p > 0.05). The other contact lens materials had stable contact angles and NIKBUT over their recommended wearing period (p > 0.05), with the exception of samfilcon A, which had an increase in contact angle after 14 days as compared to t = 0 (p < 0.05). Senofilcon A and samfilcon A also showed an increase in coefficient of friction at 14 and 30 days, respectively, compared to their blister pack values (p < 0.05). CONCLUSION: The results indicate that serafilcon A gradually depletes its reserve of PEO-PBO over 1 week, but this decrease did not significantly change the lens performance in vitro during this time frame.

Antifouling Silicone Hydrogel Contact Lenses with a Bioinspired 2-Methacryloyloxyethyl Phosphorylcholine Polymer Surface.

Inspired by the cell membrane surface as well as the ocular tissue, a novel and clinically applicable antifouling silicone hydrogel contact lens material was developed. The unique chemical and biological features on the surface on a silicone hydrogel base substrate were achieved by a cross-linked polymer layer composed of 2-methacryloyloxyethyl phosphorylcholine (MPC), which was considered important for optimal on-eye performance. The effects of the polymer layer on adsorption of biomolecules, such as lipid and proteins, and adhesion of cells and bacteria were evaluated and compared with several conventional silicone hydrogel contact lens materials. The MPC polymer layer provided significant resistance to lipid deposition as visually demonstrated by the three-dimensional confocal images of whole contact lenses. Also, fibroblast cell adhesion was decreased to a 1% level compared with that on the conventional silicone hydrogel contact lenses. The movement of the cells on the surface of the MPC polymer-modified lens material was greater compared with other silicone hydrogel contact lenses indicating that lubrication of the contact lenses on ocular tissue might be improved. The superior hydrophilic nature of the MPC polymer layer provides improved surface properties compared to the underlying silicone hydrogel base substrate.

Lipid Analysis on Block Copolymer-containing Packaging Solution and Lens Care Regimens: A Randomized Clinical Trial.

SIGNIFICANCE: Lotrafilcon B lenses packaged in and cared for with block copolymer-containing (polyoxyethylene-polyoxybutylene; EOBO) lens care solutions resulted in lower cholesterol extraction than each of the habitual silicone hydrogel lens/multipurpose solution (MPS) regimens tested. PURPOSE: This study aimed to compare the extracted cholesterol of lotrafilcon B lenses packaged in and cared for with EOBO-containing lens care solutions with the extracted cholesterol of habitual silicone hydrogel lenses cared for with MPS not containing EOBO. METHODS: In this prospective, randomized, observer-masked parallel study, habitual wearers of senofilcon C, senofilcon A, comfilcon A, and samfilcon A contact lenses using a non-EOBO MPS were randomized 1:1 to lotrafilcon B lenses packaged in and cared for with EOBO-containing solutions or to their habitual lenses and MPS. Subjects randomized to lotrafilcon B were further randomized to one of two EOBO-containing lens care solutions, OPTI-FREE PUREMOIST or CLEAR CARE PLUS with HydraGlyde (Alcon Laboratories, Inc., Fort Worth, TX). A subset of right eye lenses was collected after wear, and total cholesterol was extracted and measured using a fluorometric enzymatic assay. RESULTS: Of 143 lenses analyzed, 95 were from subjects randomized to their habitual lenses/MPS and 48 to lotrafilcon B + EOBO lenses plus CLEAR CARE PLUS with HydraGlyde or OPTI-FREE PUREMOIST. The mean amounts of cholesterol extracted from lotrafilcon B + EOBO lenses cared for with CLEAR CARE PLUS with HydraGlyde (0.28 ± 0.18 µg/lens) and OPTI-FREE PUREMOIST (0.28 ± 0.48 µg/lens) were significantly lower than those extracted from senofilcon C (4.18 ± 3.25 µg/lens), senofilcon A (2.19 ± 2.69 µg/lens), comfilcon A (2.17 ± 1.47 µg/lens), and samfilcon A (2.07 ± 1.48 µg/lens) lenses used with MPS (P < .0001 each). CONCLUSIONS: Cholesterol sorption was significantly lower in wearers of lotrafilcon B lenses cared for with polyoxyethylene-polyoxybutylene-containing lens care solutions than in users of habitual silicone hydrogel lenses cared for with non-polyoxyethylene-polyoxybutylene MPS.